Ice Green
|
Technical properties
|
Standard
|
Unit
|
Result
|
|
Compressive strength
|
EN 1926
|
Mpa
|
171
|
|
Flexural strength
|
EN 12372
|
Mpa
|
11,5
|
|
Flexural strength after 240 frost
cycles/120 days |
EN 12371
|
Mpa
|
10,4
|
|
Abrasion resistance, Böhme
|
DIN 52108
|
cm³/50cm²
|
8
|
|
Abrasion resistance, Böhme
|
EN 14157
|
mm³
|
0,2
|
|
Water absorption
|
EN 13755
|
vikt %
|
0,28
|
|
Apparent density
|
EN 1936
|
kg/ m³
|
2677
|
|
Open porosity
|
EN 1936
|
%
|
0,74
|
|
Breaking load at dowel holes 30mm
|
EN 13364
|
N
|
2420
|
|
Breaking load at dowel holes 50mm
|
EN 13364
|
N
|
4200
|
|
Slip resistance, honed surface
|
EN 14231
|
SRV, torr (dry)
|
Value
|
|
Slip resistance, honed surface
|
EN 14231
|
SRV, våt (wet)
|
|
|
Rupture energy Thickness 20mm
|
EN 14158
|
J
|
7,0
|
|
Rupture energy Thickness 50mm
|
EN 14158
|
J
|
27,0
|
|
Petrographic composition
|
EN 12407*
|
||
|
Potassium feldspar
|
%
|
10
|
|
|
Plagioclase
|
%
|
44
|
|
|
Quartz
|
%
|
20
|
|
|
Biotite
|
%
|
6
|
|
|
Epidote
|
%
|
10
|
|
|
Muscovite
|
%
|
7
|
|
|
Pyrite
|
%
|
3
|
(Test results from SINTEF Building and Infrastucture Institute)
* Only mineral composition, main mineral and possibly shell and skeleton so-called fossil (Only main components)
1) Based on thickness measurement
2) Based on weight measurement
* Only mineral composition, main mineral and possibly shell and skeleton so-called fossil (Only main components)
1) Based on thickness measurement
2) Based on weight measurement